UV photosensitive melted glasses

ABSTRACT

The present invention relates generally to UV (ultraviolet) photosensitive bulk glass, and particularly to batch meltable alkali boro-alumino-silicate and germanosilicate glasses. The photosensitive bulk glass of the invention exhibits photosensitivity to UV wavelengths below 300 nm.  
     The photosensitivity of the alkali boro-alumino-silicate and germanosilicate bulk glasses to UV wavelengths below 300 nm provide for the making of refractive index patterns in the glass. With a radiation source below 300 nm, such a laser, refractive index patterns are formed in the glass. The inventive photosensitive optical refractive index pattern forming bulk glass allows for the formation of patterns in glass and devices which utilize such patterned glass.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

[0001] The present application is a continuation-in-part of U.S. patent application Ser. No. 10/099,088, filed Mar. 15, 2002, to Borrelli et al., and entitled “UV Photosensitive Melted Glasses,” which is a continuation-in-part of U.S. patent application Ser. No. 09/874,342, filed Jun. 5, 2001, to Borrelli, et al, and entitled “UV Photosensitive Melted Germano-Silicate Glasses,” which claims the priority of U.S. Provisional Patent Application Serial No. 60/221,811, filed Jul. 31, 2000. The inventions described in these applications are assigned to the assignee of the present invention, and the disclosure of these applications are incorporated by references herein and for all purposes.

FIELD OF THE INVENTION

[0002] The present invention relates generally to photosensitive bulk glass, and particularly to meltable alkali boro-alumino-silcate and germanosilicate glasses.

BACKGROUND OF THE INVENTION

[0003] Optical transmission systems, including optical fiber communication systems, have become an attractive alternative for carrying voice and data at high speeds. While the performance of optical communication systems continues to improve, there is increasing pressure on each segment of the optical communication industry to reduce costs associated with building and maintaining an optical network.

[0004] Quite often, optical communication systems require various types of optical filter elements. For example, diffractive filter elements may be used to effect the separation (demultiplexing) of individual wavelength channels in a wavelength division multiplexed (WDM) optical system. In addition, these refractive filter elements may be used to compensate for the ill-effects of dispersion, to include chromatic dispersion (CD) and polarization mode dispersion (PMD).

[0005] One type of diffractive optical filter is a Bragg grating. Bragg gratings are interferometric optical devices which have been employed in a variety of applications including multiplexing/demultiplexing applications and dispersion compensation applications. Bragg gratings may be used to reflect light of a wavelength which satisfies the Bragg phase matching condition, and which transmits all other wavelengths.

[0006] One useful technique for forming a Bragg grating is to selectively alter the index of refraction in a substrate in a periodic manner. This selective alteration of the index of refraction can be used to fabricate both Bragg gratings in which the period of the index of refraction is regular, as well as chirped gratings in which the period of the index of refraction varies as a function of distance.

[0007] What is needed is a batch meltable glass material which is photosensitive, and which overcomes certain drawbacks of conventional glass materials.

SUMMARY OF THE INVENTION

[0008] The invention includes a photosensitive glass. According to an exemplary embodiment of the present invention a meltable photosensitive glass has a hydrogen content of greater than 10¹⁷ hydrogen molecules/cm³. The refractive index change in the exposed portions of the glass is 10⁻⁴ (Δn>10⁻⁴) measured at a wavelength of 633 nm; and the glass is photosensitive to light having a wavelength of less than 300 nm.

[0009] According to another exemplary embodiment of the present invention, the starting glass is a photosensitizable alkali boro-alumino-silicate glass that can be loaded with hydrogen to make it photosensitive. In one exemplary embodiment of the present invention, the glass is a below 300 nm photosensitive glass which has a composition of 40-80 mole % SiO₂, 2-15 mole % GeO₂, 10-36 mole % B₂O₃, 1-6 mole % Al₂O₃ and 2-10 mole % R₂O where R is chosen from the alkali elements with the glass exhibiting photosensitivity to below 300 nm wavelengths. In another exemplary embodiment of the present invention, the glass has a composition including approximately 25 weight % to approximately 45 weight % SiO₂, approximately 3 weight % to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F, with the glass exhibiting photosensitivity to below 300 nm wavelengths.

[0010] Another exemplary embodiment of the present invention includes a molecular hydrogen loadable photosensitive bulk glass. The photosensitive bulk glass is an alkali boro-alumino silicate glass with a melting temperature no greater than 1650° C. Preferably, the glass has a batch composition comprising no greater than 85 mole % SiO₂, no less than 10 mole % B₂O₃, no less than 2 mole % GeO₂, and a combined alkali and alumina content no greater than 20 mole % Al₂O₃+alkali with the glass having a molecular hydrogen loadable level of at least 10¹⁸H₂ molecules/cm³.

[0011] Another exemplary embodiment of the present invention includes a meltable photosensitive germanosilicate glass material having a hydrogen content less than 10¹⁷H₂ molecules/cm³. In one exemplary embodiment of the invention, the glass is a below 300 nm photosensitive glass which has a composition of 40-80 mole % SiO₂, 2-15 mole % GeO₂, 10-36 mole % B₂O₃, 1-6 mole % Al₂O₃ and 2-10 mole % R₂O where R is chosen from the alkali elements with the glass exhibiting photosensitivity to below 300 nm wavelengths. In another exemplary embodiment of the invention, the glass includes approximately 25 weight % to approximately 45 weight % SiO₂, approximately 3 weight % to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F, with the glass exhibiting photosensitivity to below 300 nm wavelengths.

[0012] Another exemplary embodiment of the present invention includes a method of making a refractive index pattern. The invention includes providing a photosensitive bulk glass having a 300 nm absorption less than 20 dB/cm, providing a radiation source below 300 nm, forming a pattern with the below 300 nm radiation, and exposing the photosensitive bulk glass to the pattern to form a modulated refractive index pattern in the bulk glass.

[0013] Another exemplary embodiment of the present invention includes a method of making a molecular hydrogen loadable photosensitive glass optical device preform. Preferably, the method comprises making a refractive index pattern preform out of melted glass. The method includes providing a germania silica glass powder batch with transition metal contamination level ≦1 ppm by heavy metals. The method includes melting contamination level ≦1 ppm by weight for heavy metals. The method includes melting the silica glass powder batch to form a homogeneous glass melt, cooling the glass melt into a UV transmitting bulk glass having a 300 nm absorption less than 20 dB/cm and forming the bulk glass into an optical device preform in which refractive index patterns can be made.

[0014] Another exemplary embodiment of the present invention includes a photosensitive glass optical refractive index pattern preform for use with UV light in the formation of refractive index patterns. The preform is comprised for use with UV light in the formation of refractive index patterns. The preform is comprised of an alkali boro-alumino-silicate glass with a 300 nm absorption less than 20 dB/cm. The preform glass has a UV wavelength inducable modulated refractive index Δn level greater than 10⁻⁵ with a molecular hydrogen level of at least 10¹⁸H₂ molecules/cm³.

BRIEF DESCRIPTION OF THE DRAWINGS

[0015] The invention is best understood from the following detailed description when read with the accompanying drawing figures. It is emphasized that the various features are not necessarily drawn to scale. In fact, the dimensions may be arbitrarily increased or decreased for clarity of discussion.

[0016]FIG. 1 is a plot of absorbance/nm versus UV wavelength (nm) (200-300 nm) in accordance with the invention.

[0017]FIG. 2a is a plot of induced modulated refractive index [Δn(×10⁻⁴)] versus UV exposure time (minutes) in accordance with the invention.

[0018]FIG. 2b is a plot of induced modulated refractive index [Δn(×10⁻⁴)] versus UV exposure fluence [mJ/cm²] in accordance with the invention.

[0019]FIG. 3 is a photosensitivity thermal stability plot diffraction efficiency of induced refractive index changes in the bulk glass versus hours heated at 400° C. in accordance with the invention.

[0020]FIG. 4 is a plot induced refractive index [Δn] versus OH concentration in accordance with the invention. FIG. 4 inset is a plot of absorbance versus wave numbers (cm⁻¹) showing OH stretching vibrations and absorbance before (dashed line) and after (solid line) a 90 minute UV exposure of 20 mJ/cm²/pulse.

[0021]FIG. 5 is a plot of absorbance versus UV wavelength (nm) before (dashed line) and after (solid line) the 90 minute UV exposure of 20 mJ/cm²/pulse of FIG. 4.

[0022]FIG. 6 is a plot of intensity (dBm) versus wavelength (1545 nm-1559 nm) of refractive index pattern grating formed in the bulk glass in accordance with the invention. FIG. 6 inset show the geometry of the UV exposure and the reflectivity and transmission measurements of the plot.

[0023]FIG. 7 illustrates the refractive index pattern grating of FIG. 6. FIG. 7a is a cross-section showing the refractive index pattern grating in the bulk glass.

[0024]FIG. 8 illustrates a method in accordance with the invention.

[0025]FIG. 9 illustrates a method in accordance with the invention.

[0026]FIG. 10 is a tabular representation of glass composition in accordance with an exemplary embodiment of the present invention.

DETAILED DESCRIPTION

[0027] In the following detailed description, for purposes of explanation and not limitation, exemplary embodiments disclosing specific details are set forth in order to provide a thorough understanding of the present invention. However, it will be apparent to one having ordinary skill in the art having had the benefit of the present disclosure, that the present invention may be practiced in other embodiments that depart from the specific details disclosed herein. Moreover, descriptions of well-known devices, methods and materials may be omitted so as to not obscure the description of the present invention.

[0028] It is noted also that the refractive index change (Δn) as referenced herein is measured at 633 nm. In many occurances this is specifically noted. However, if not specifically noted at a particular occurance, it is understood that the index change is measured at 633 nm.

[0029] Briefly, the present invention relates to meltable photosensitive glass materials. According to an exemplary embodiment of the present invention, a meltable photosensitive glass material has a molecular hydrogen content that is greater than 10¹⁷ hydrogen molecules/cm³. When exposed to light having a wavelength of less than 300 nm, the refractive index change in the exposed portions of the photosensitive glass material is less than 10⁻⁴ (Δn<10⁻⁴) (measured at 633 nm). Usefully, gratings, as well as other structures, may be formed in the glass material by selective exposure of the glass material to light of a wavelength range at which the glass material is photosensitive. The glass may be a germanosilicate glass. Germanosilicate glasses generally have a GeO₂ content of at least 2 weight %, and a SiO₂ content of at least 20 weight %. In one illustrative embodiment of the present invention, the GeO₂ content of the germanosilicate glasses of the present invention is at least 6 weight %.

[0030] According to an exemplary embodiment, the present invention comprises a below 300 nm UV light photosensitizable glass with 40-80% SiO₂, 2-15 mole % GeO₂, 10-36 mole % B₂O₃, 1-6 mole % Al₂O₃ and 2-10 mole % R₂O wherein R is an alkali, with the glass photosensitive when loaded with hydrogen. Preferably, the glass comprises 42-73 mole % SiO₂, 2-15% mole % GeO₂, 25-36 mole % B₂O₃, 2-6 mole % Al₂O₃, and 2-6 mole % R₂O. Usefully, the glass comprises 42-67 mole % SiO₂, 2-15 mole % GeO₂, 25-36 mole % B₂O₃, 2-6 mole % Al₂O₃, and 2-6 mole % R₂O. Preferably R₂O is at least one alkali oxide chosen from the group of Na, Li, and K. In an embodiment R is Na. In another exemplary embodiment R is Li. In a further exemplary embodiment R is K. Moreover, in embodiments of the invention the R alkali content of the glass includes mixtures of Na, Li, and K. Preferably, the glass has an alkali/alumina mole ratio in the range of 1±0.5. Usefully, the glass is essentially free of non-bridging oxygen ions and such are minimized and inhibited by the glass components.

[0031] The invention further includes a molecular hydrogen loadable photosensitive bulk glass comprised of an alkali boro-alumino-silicate glass with a melting temperature ≦1650° C. Preferably the alkali boro-alumino-silicate glass has a batch composition of ≦85 mole % SiO₂, ≧10 mole % B₂O₃, ≧2 mole % GeO₂, and a combined alkali and alumina content <20 mole % Al₂O₃+R₂O. Preferably the batch composition is ≦80 mole % SiO₂ and ≧20 mole % B₂O₃. More preferably the batch composition has ≦70 mole % SiO₂ and 25 mole B₂O₃. Preferably the glass has a batch composition with a combined alkali and alumina content <16 mole Al₂O₃+R₂O.

[0032] In another illustrative embodiment of the present invention, the photosensitizable bulk glass is a germanosilicate glass having approximately 25 weight % to approximately 45 weight % SiO₂, approximately 3 weight % to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F, with the glass photosensitive when loaded with hydrogen. Illustratively, the glass comprises approximately 30 weight % to approximately 40 weight % SiO₂. Illustratively the glass has a GeO₂ content of approximately 7 weight % to approximately 17 weight %. Illustratively the glass has a B₂O₃ content of approximately 10 weight % to approximately 22 weight %. Illustratively the glass has an Al₂O₃ content of approximately 10 weight % to approximately 19 weight %. Illustratively the glass has an R₂O content of approximately 10 weight % to approximately 20 weight %. Illustratively, the glass has a F content of greater than about 5 weight %. Illustratively R₂O is at least one alkali chosen from the group of Na, Li, and K. In an embodiment R is Na. In another exemplary embodiment R is Li. In a further exemplary embodiment R is K. Moreover, in embodiments of the invention the R alkali content of the glass includes mixtures of Na, Li, and K. Preferably, the glass has an alkali/alumina mole ratio (mole % R₂O/mole % Al₂O₃) in the range of approximately 0.5 to approximately 1.5. Usefully, the glass is essentially free of non-bridging oxygen ions and such are minimized and inhibited by the glass components.

[0033] In accordance with an exemplary embodiment of the present invention, the photosensitizable glass has a hydrogen content that is ≧10¹⁷H₂ molecules/cm³. The hydrogen may be loaded in the glass by known techniques.

[0034] It is noted that according to an exemplary embodiment the glass has a loadable hydrogen content ≧10¹⁹H₂ molecules/cm³. Preferably, the glass is loadable and loaded with at least 2×10¹⁹H₂ molecules/cm³, and preferably the hydrogen content is preferably at least 5×10¹⁹ hydrogen molecules/cm³ according to another exemplary embodiment. Such hydrogen load levels are preferably achieved with a hydrogen loading temperature no greater than 200° C. with the molecular hydrogen entering the glass as molecular hydrogen (H₂) and remaining as molecular hydrogen in the glass in that the hydrogen molecules contained in the glass do not disassociate and react with the glass until irradiated.

[0035] The photosensitizable glass has a transition metal contaminant level ≦1 ppm by weight for transition metal contaminants. The glass also has a heavy metal contaminant level ≦1 ppm by weight for heavy metal contaminants. Preferably the glass has a Fe content ≦1 ppm by weight Fe, and more preferably <1 ppm by weight Fe. Preferably the glass has a Ti content ≦1 ppm by weight Ti, and more preferably <1 ppm by weight Ti. The photosensitizable glass has a 300 nm absorption less than 30 dB/cm, usefully less than 20 dB/cm, and more preferably less than 15 dB/cm. Even more preferred the 250 nm absorption is 10 dB/cm and most preferably <5 dB/cm.

[0036] Preferably the photosensitizable glass is melted glass, and most preferably a non-sintered glass. The glass has a melting temperature ≦1650° C., and preferably ≦1600° C. which provides for formation by melting a mixed batch of glass feedstock powders for form a homogeneous glass melt which can be cooled into the glass. Preferably the glass has a melting temperature ≦1550° C., and more preferably ≦1500° C. Preferably the glass has a softening temperature ≦700° C. Such glass forming temperatures allow for efficient and economic manufacturing of the glass and avoid the complications of sintering and sintered glass compositions.

[0037] Preferably the glass has a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴ (measured at 633 nm) where the exposure wavelength is no greater than 300 nm and the glass has a molecular hydrogen content >10¹⁷H₂ molecules/cm³. According to an exemplary embodiment, the inventive glass exhibits photosensitivity as a consequence of exposure to light of no greater then 300 nm wavelength induced modulated refractive index Δn>10⁻⁴ when loaded with a molecular hydrogen content >10¹⁹ molecules/cm³. It is noted that the preferable exposure wavelength range to induce the above referenced wavelength induced modulated refractive index is approximately 248 nm to approximately 265 nm. Preferably the glass has a modulated refractive index Δn>2×10⁻⁴ when hydrogen loaded. It is further noted that the exposure wavelength may be as low as 244 nm.

[0038] Preferably the photosensitive bulk glass is essentially free of transition metals and with a 300 nm absorption less then 30 dB/cm. Preferably, the transition metal contaminant levels are below 1 ppm by weight, with the iron content <1 ppm by weight and more preferably <0.1 ppm by weight. Preferably the titanium content is <1 ppm by weight, and more preferably <0.1 ppm. Preferably the bulk glass has 300 nm absorption <20 dB/cm, more preferably <15 dB/cm, more preferably <10 dB/cm, and most preferred <5 dB/cm. It is noted that it is useful to minimize the impurity levels of iron, other transition metals and OH. Low concentrations of these impurities aids in reducing loss, which will improve the uniformity of gratings formed in the glass materials in accordance with an exemplary embodiment of the present invention.

[0039] The glass has a refractive index photosensitivity level modulated Δn>10⁻⁵ (measured at 633 nm) with a loaded molecular hydrogen content ≧10¹⁸H₂ molecules/cm³. Such a Δn can be achieved with a 248 nm KrF excimer laser UV exposure of 90 minutes at 12 mJ/cm²/pulse. Preferably the glass has a refractive index photosensitivity level Δn>10⁻⁴ with a loaded molecular hydrogen content ≧10¹⁹H₂ molecules/cm³. Preferably the bulk glass is loadable with molecular hydrogen to a molecular hydrogen loaded level of at least 10¹⁹H₂ molecules/cm³ with a hydrogen loading temperature ≦200° C. Preferably the glass has a molecular hydrogen content >10¹⁹H₂ molecules/cm³ and a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴(measured at 633 nm).

[0040] The bulk glass is a non-sintered glass, and preferably has a melting temperature ≦1,600° C., and more preferred ≦1,550° C. Preferably the glass is a cooled fluid melt mixture formed from a fluid melt, preferably with the fluid melt formed by melting glass batch feedstock powders. In a preferred embodiment the bulk glass is a homogeneous glass device preform body with a homogeneous composition with glass dopants evenly spread throughout the glass body. Preferably the preform body has a homogeneous index of refraction and is free of pre-radiated core and claddings regions with a homogeneous distribution of glass component elements.

[0041] The present invention also includes meltable germanosilicate glasses that are photosensitive in the absence of hydrogen or at low levels of hydrogen loading (for example, less than approximately 10¹⁷H₂ molecules/cm², illustratively less than approximately 10¹⁴H₂ molecules/cm³.) These germanosilicate glasses have a GeO₂ content of at least 2 weight % (illustratively at least 6 weight %), and a SiO₂ content of at least 20 weight %. Preferably, the meltable germanosilicate glasses have melting temperatures of ≦1650° C., more preferably ≦1550° C., and most preferably ≦1500° C. Illustratively, the glasses have a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴.

[0042] An exemplary embodiment of the present invention comprises a below 300 nm UV light photosensitive glass with approximately 40 mole % to approximately 80 mole % SiO₂, approximately 2 mole % to approximately 15 mole % GeO₂, approximately 10 mole % to approximately 36 mole % B₂O₃, approximately 1 mole % to approximately 6 mole % Al₂O₃ and approximately 2 mole % to approximately 10 mole % R₂O wherein R is an alkali, with the glass photosensitive in the absence of hydrogen and at low hydrogen loadings. Illustratively, the glass comprises approximately 42 mole % to approximately 73 mole % SiO₂, approximately 2 mole % to approximately 15% mole % GeO₂, approximately 25 mole % to approximately 36 mole % B₂O₃, approximately 2 mole % to approximately 6 mole % Al₂O₃, and approximately 2 mole % to approximately 6 mole % R₂O. Usefully, the glass comprises approximately 42 mole % to approximately 67 mole % SiO₂, approximately 2 mole % to approximately 15 mole % GeO₂, approximately 25 mole % to approximately 36 mole % B₂O₃, approximately 2 mole % to approximately 6 mole % Al₂O₃, and approximately 2 mole % to approximately 6 mole % R₂O. Illustratively, R is at least one alkali chosen from the group of Na, Li, and K. In one exemplary embodiment R is Na. In another exemplary embodiment R is Li. In a further exemplary embodiment R is K. Moreover, in embodiments of the invention the R alkali content of the glass includes mixtures of Na, Li, and K. Preferably, the glass has an alkali/alumina mole ratio in the range of approximately 0.5 to approximately 1.5. Usefully, the glass is essentially free of non-bridging oxygen ions and such are minimized and inhibited by the glass components.

[0043] In another embodiment of the present invention, the photosensitive bulk glass may be a germanosilicate glass having approximately 25 weight % to approximately 45 weight % SiO₂, approximately 3 weight % to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F, with the glass photosensitive in the absence of hydrogen and or at low hydrogen loadings. Illustratively, the glass comprises approximately 30 weight % to approximately 40 weight % SiO₂. Illustratively the glass has a GeO₂ content of approximately 7 weight % to approximately 17 weight %. Illustratively the glass has a B₂O₃ content of approximately 10 weight % to approximately 22 weight %. Illustratively the glass has an Al₂O₃ content of approximately 10 weight % to approximately 19 weight %. Illustratively the glass has an R₂O content of approximately 10 weight % to approximately 20 weight %. Illustratively, the glass has a F content of greater than about 5 weight %. Illustratively R₂O is at least one alkali chosen from the group of Na, Li, and K. In an embodiment R is Na. In another exemplary embodiment R is Li. In a further exemplary embodiment R is K. Moreover, in embodiments of the invention the R alkali content of the glass includes mixtures of Na, Li, and K. Preferably, the glass has an alkali/alumina mole ratio (mole % R₂ 0/mole % Al₂O₃) in the range of approximately 0.5 to approximately 1.5. Usefully, the glass is essentially free of non-bridging oxygen ions and such are minimized and inhibited by the glass components.

[0044] The photosensitive glass has a transition metal contaminant level >1 ppm by weight for transition metal contaminants. The glass also has a heavy metal contaminant level ≦1 ppm by weight for heavy metal contaminants. Preferably the glass has a Fe content ≦1 ppm by weight Fe, and more preferably <1 ppm by weight Fe. Preferably the glass has a Ti content ≦1 ppm by weight Ti, and more preferably <1 ppm by weight Ti. The photosensitive glass has a 300 nm absorption less than 30 dB/cm, usefully less than 20 dB/cm, and more preferably less than 15 dB/cm. Even more preferred the 250 nm absorption is 10 dB/cm and most preferably <5 dB/cm.

[0045] Preferably the photosensitive glass is melted glass, and most preferably a non-sintered glass. The glass has a melting temperature ≦1650° C., and preferably ≦1600° C. which provides for formation by melting a mixed batch of glass feedstock powders for form a homogeneous glass melt which can be cooled into the glass. Preferably the glass has a melting temperature ≦1550° C., and more preferably ≦1500° C. Preferably the glass has a softening temperature ≦700° C. Such glass forming temperatures allow for efficient and economic manufacturing of the glass and avoid the complications of sintering and sintered glass compositions. In a preferred embodiment the bulk glass is a homogeneous glass device preform body with a homogeneous composition with glass dopants evenly spread throughout the glass body. Preferably the preform body has a homogeneous index of refraction and is free of pre-radiated core and claddings regions with a homogeneous distribution of glass component elements.

[0046] Illustratively, the glass has a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴ (measured at 633 nm) where the exposure wavelength is no greater than 300 nm and the glass has no or low hydrogen loading. According to an exemplary embodiment, the inventive glass exhibits photosensitivity as a consequence of exposure to light of no greater then 300 nm wavelength induced modulated refractive index Δn>10⁻⁴. It is noted that the preferable exposure wavelength range to induce the above referenced wavelength induced modulated refractive index is approximately 248 nm to approximately 265 nm. Preferably the glass has a modulated refractive index Δn>2×10⁻⁴. It is further noted that the exposure wavelength may be as low as 244 nm. The low or no hydrogen loaded photosensitive glasses may require a higher level of irradiation to yield an index change equivalent to that of the analogous hydrogen-loaded glass. For example, under a given UV fluence, a photosensitive glass may achieve an index change of 10⁻⁴ after 8 minutes when hydrogen loaded, and after 64 minutes in the absence of hydrogen.

[0047] The invention includes a method of making a refractive index pattern. Preferably the method comprises making a refractive index pattern grating. The method of making a pattern includes providing a photosensitive bulk glass having a 300 nm absorption less than 30 dB/cm, preferably less than 20 dB/cm. The method includes providing a below 300 nm radiation source and producing below 300 nm radiation. The method includes forming a pattern with the below 300 nm radiation and exposing the photosensitive bulk glass to the pattern to form a modulated refractive index pattern in the bulk glass. Preferably the provided bulk glass has a <15 dB/cm absorption at 300 nm, more preferably <10 dB/cm, and most preferably <5 dB/cm. Forming the pattern preferably comprises forming a pattern and exposing the bulk glass to the pattern for form a modulated refractive index grating in the bulk glass.

[0048] Providing the photosensitive bulk glass preferably includes providing an alkali boro-alumino-silicate glass. The provided bulk glass body preferably is homogeneous in composition and refractive index and does not have separate core/cladding regions.

[0049] Providing the photosensitive bulk glass includes providing a non-sintered glass, with the glass being a melted glass. Preferably the glass is a melted glass with a melting temperature ≦1,650° C. More preferably the melting temperature of the bulk glass ≦1,600° C., more preferred ≦1,550° C., and most preferred ≦1,500° C. Providing the photosensitive bulk glass includes providing an alkali boro-alumino-silicate glass batch and melting the glass batch to form an alkali boro-alumino-silicate glass melt. The method includes cooling the glass melt into the bulk glass. Preferably melting includes containing the glass melt in a heated glassy fluid state and forming the glass melt into a coolable body, such as delivering the glass melt through an orifice and to a cooling site.

[0050] In one embodiment of the present invention, the provided bulk glass may be a molecular hydrogen loadable bulk glass. Preferably the method includes providing a melted bulk glass and loading the bulk glass with at least 10¹⁸H₂ molecules/cm³. Preferably loading the bulk glass includes loading with at least 10¹⁹H₂ molecules/cm³, and more preferably at least 5×10¹⁹H₂ molecules/cm³. Loading bulk glass is preformed with a molecular hydrogen loading temperature <200° C. Preferably the hydrogen loading temperature ≦150° C., more preferably ≦100° C. Preferably a hydrogen load atmosphere of at least 20 atmospheres of hydrogen are used, and most preferably at least 100 atmospheres of H₂ is utilized to dope the bulk glass. Such loading can be achieved in high temperature vessels that contain the H₂ gas and the bulk glass. Preferably the bulk glass body has a glass body physical size with glass volume and surface area to provide efficient loading of hydrogen, preferably with the bulk glass body being a near net shape of the preform and optical device it is made into. The bulk glass is exposed to the H₂ gas pressurized atmosphere for a H₂ loading time sufficient and effective such that the center of the bulk glass body has a molecular hydrogen concentration that is at least 90% of the ambient H₂ loading atmosphere. As the skilled artisan will appreciate, the provided bulk glass may also be a glass that is photosensitive in the absence of hydrogen loading or at low hydrogen loadings.

[0051] Exposing the photosensitive bulk glass preferably includes exposing the glass to form a pattern by inducing a refractive index Δn≧10⁻⁵, and most preferably Δn≧10⁻⁴ (again measured at 633 nm).

[0052] The invention includes a method of making a molecular hydrogen loadable photosensitive glass optical device preform. The method of making the preform includes providing a germania silica glass batch with a transition metal contamination level ≦1 ppm by weight for heavy metals. The method includes melting the silica glass batch to form a homogeneous glass melt, cooling the glass melt into a UV transmitting bulk glass having a 300 nm absorption less than 20 dB/cm and forming the bulk glass into an optical device preform. Forming the bulk into an optical device preform may include loading the bulk glass with molecular hydrogen to a level of at least 10¹⁸H₂ molecules/cm³, and more preferably at least 10¹⁹H₂ molecules/cm³.

[0053] Providing the germania silica glass batch includes providing an alkali boro-alumino-silicate glass batch and melting the glass at a melting temperature ≦1,650° C. Preferably melting comprises melting at ≦1,600° C., more preferably ≦1,550° C., and most preferably ≦1,500° C. The method of making preferably includes pouring the glass melt to form bulk glass bodies, and more preferably includes delivering the glass melt through a glass forming orifice. Making the bulk glass performs preferably includes forming a preform glass body with a smallest size dimension that is greater than 5 μm.

[0054] The invention further includes a photosensitive glass optical refractive index pattern preform for use with UV light in the formation of refractive index patterns. The inventive preform is comprised of an alkali boro-alumino-silicate glass with a 300 nm absorption less than 20 dB/cm. The preform has a below 300 nm UV wavelength inducible modulated refractive index Δn≧10⁻⁵ with the bulk glass exhibiting photosensitivity as a consequence of exposure to light of 300 nm or less. The glass may have a molecular hydrogen level of at least 10¹⁸H₂ molecules/cm³ during the exposure. Preferably the refractive index pattern preform has a UV wavelength inducible modulated refractive index Δn level >10⁻⁴ with a molecular hydrogen level of at least 10¹⁹H₂ molecules/cm³. Preferably the bulk glass preform has a 300 nm absorption less than 15 dB/cm, more preferably less than 10 dB/cm, and most preferred less than 5 dB/cm. Preferably the alkali boro-alumino-silicate glass preform is a non-sintered glass body formed by a melting process is result in a melted glass.

EXAMPLES

[0055] The invention includes a large UV-induced refractive index change in a melted alkali-alumino-boro-germano-silicate composition that has been loaded with molecular hydrogen. The UV exposures utilized include CW 244-nm light and a pulsed KrF excimer laser at 248-nm. It is noted that a tuneable Nd/YAG laser which emits radiation at 268 nm, 270 nm, 280 nm and 290 nm could be used in place of the KrF excimer laser. A modulated refractive index of the order of 2-3×10⁻⁴ has been measured (at 633 nm) in the bulk glass.

[0056] It is believed that the ability to load with molecular hydrogen, and the photoreaction, depends on the composition of the glass. The UV spectroscopy of the bulk glass before and after exposure, as well as the magnitude of the induced refractive index correlates well with the growth of the OH absorption as measured in the IR (OH stretching vibrations).

[0057] As shown in FIG. 6, a Bragg grating was made in a bulk glass ample (Glass 5 g, Glass Composition Table) by exposing through a phase mask from the top face, with a measured transmission and reflectivity as shown.

[0058] In order to provide melted glasses, the invention utilizes various constituents to make the glass softer and lower the melting temperature. This includes using constituents like alkali, alumina and boron to lower the melting temperature and to decrease the viscosity. In a preferred embodiment the glass batch melting temperature is lowered by using a sufficient amount of a fluoride of the glass components to lower the melting temperature. For example with Glass 4 b (See Glass Composition Table of FIG. 10) aluminum fluoride is utilized with a F batch composition of about 3.3 wt. %. In a preferred embodiment the batch composition melting temperature is lowered with a batch composition incorporating of fluorine at a batch wt. % of ≦10 weight % F, illustratively ≦6 weight % F. The lowering of the melting temperature is done in such a way as not to move the fundamental absorption beyond 248-nm (5-eV).

[0059] The fundamental absorption edge of pure silica, for example, is determined by the transition from the band consisting of the overlapping 2p oxygen orbitals (valence band) to the band made up from the sp³ non-bonding orbitals of silicon (conduction band). The addition of alkali introduces another set of levels associated with non-bridging oxygen. When the concentration is high enough, a new band appears above that of the original valence band, thus moving the fundamental absorption edge to longer wavelengths. On the other hand, the addition of the network substitution ions such as boron, aluminum, and germanium has much less influence on the absorption edge.

[0060] Impurities such as transition metal ions or heavy metal ions that are inadvertently incorporated into glass, either from the batch materials, the containment crucible, the furnace or forming, must be kept to the <1 ppm level. These ions, even in small amounts have a dramatic adverse effect on the UV-absorption edge.

[0061] The invention includes making a SiO₂-GeO₂ bulk glass that can be melted and formed in a conventional batch way be limiting the additional constituents sufficiently so as to maintain high transparency at 248-nm, and yet achieve melting at a reasonable temperature (1650° C.) and a softening temperature of approximately of 600° C. (softening temperature below 700° C. preferred).

[0062] Glasses were made from pure starting materials, in particular low iron content sand. They were melted in clean platinum crucibles at 1,550° C. for 16 hours. In the initial sampling procedure, the glass was poured into patties and annealed. Subsequently, the quality of the glass was improved in terms of (striae) defects and cords by using semi-continuous melting where the glass is not poured from a melt crucible which is the source of much of the striae, but delivered through an orifice.

[0063] The hydrogen loading was done in a Parr™ pressurized reactor using 150° C. loading temperature at 100 atm pressure. The IR spectroscopy was done with a Nicolet™ FTIR spectrometer to determine the molecular hydrogen (H₂) content.

[0064] The effect on the absorption spectrum with change in GeO₂ content for alkali-alumino-boro-silicate glass family of R₂O (3-4 mole %), Al₂O₃ (3-4 mole %), B₂O₃ (25-35 mole %), GeO₂ (2.5-15 mole %), and SiO₂ (66.5-42 mole %) is shown in FIG. 1. In all cases we were able to maintain high transmittance at below 300 nm wavelength of 248-nm which was to be the UV exposure excitation wavelength.

[0065] We exposed samples from each system to pure hydrogen ambient at 100 atm at 150° C. in order to impregnate the samples with molecular hydrogen. The higher temperature was used to speed up the diffusion process for samples that were a few millimeters thick and yet not allow the thermal reaction to occur. We used IR spectroscopy to determine the molecular hydrogen content. Photosensitivity was achieved with the inventive glasses that had a loaded molecular hydrogen content. Hydrogen load levels up to 5×10¹⁹H₂ molecules/cm³ were obtained with the inventive glass.

[0066] In order to measure the UV-induced photosensitivity, we hydrogen loaded 0.5-mm thick bulk glass samples. We then exposed them through a chrome absorption mask with a 10 μm grating pitch. The UV exposure source was a KrF excimer laser operating at 248-nm. The peak fluence was from 20-60 mJ/cm²/pulse at 50 Hz for periods of time running from 5-120 min.

[0067] After the UV exposure, the sample was illuminated by a spatially filtered He-Ne laser and the diffraction efficiency of the induced phase grating was measured from the ratio of the intensity of the 1^(st) to 0^(th) order. As long as the diffraction efficiency is relatively weak one can use the following simple formula for efficiency. $\begin{matrix} {{Eff} = \left( \frac{\pi \quad \Delta \quad {nL}}{\lambda} \right)^{2}} & (1) \end{matrix}$

[0068] Here, Δn is the modulated refractive index change (n=n₀+Δn cos(2πz/Λ)), L is the grating index and Λ is the period of the index pattern.

[0069] The range of measured values of the induced refractive index after a fixed 248-nm UV exposure was from 1×10⁻⁴ to 3×10⁻⁴ for the inventive alkali-alumino-boro-silicate glasses. The induced modulated refractive index as a function of the exposure time at fixed fluence is shown in FIG. 2a. FIG. 2b shows the measured induced index as a function of fluence at fixed time. The later is well represented by using the square of the fluence.

[0070] A set of glasses with fixed germania content was loaded with H₂ and UV exposed at 248-nm. The Glass Composition Tables gives the compostion, relative amounts of H₂ incorporated and the 248-nm excimer laser induced refractive index change for the set.

[0071] The thermal stability of the induced refractive index change was investigated by heating a sample having a grating and re-measuring the grating efficiency with time at temperature. The change with time after heating to 400 degrees is shown in FIG. 3.

[0072] We have produced UV-induced refractive index changes in melted non-sintered bulk glasses, similar in magnitude to that seen in vapor deposition sintered flame or plasma prepared glasses, when a high concentration of molecular hydrogen can be obtained. This follows directly from our observation that preferred melted glasses where we see molecular H₂ (>10¹⁸/cm³, as estimated by IR spectroscopy) we preferably obtain a measureable UV-induced refractive index change.

[0073] The mechanism for the molecular-mediated UV-induced photosensitivity seems to be consistent with that proposed for the hydrogen mediated effect found in the SiO₂-GeO₂ material prepared by methods other than melting such as vapor deposition and sintering. FIG. 4 shows the relationship of the increase in hydroxyl concentration (measured from the OH stretching vibration; see inset) with the induced refractive index also as shown in FIG. 5. This is also a large change in UV absorption after exposure.

[0074] We have observed stress that derives from the UV-exposure. This suggests that a volume change is occurring. From the sign of the birefringence we determine that the volume change corresponds to a densification. The refractive index contribution computed from this effect is small compared to the overall measured Δn.

[0075] As shown in FIG. 6, a bulk glass sample of Glass 5 g of the Glass Composition Table (glass block of 5×5×3 mm³) was exposed through the wide face using a 244-nm CW laser (0.35W for preferred UV exposure time of 30-60 minutes) utilizing a phase mask with a period such as to satisfy the Bragg condition at 1,550-nm to produce a refractive index pattern. The grating length was 2.5-nm. The reflectivity and transmission of the grating is shown in FIG. 6. The inset shows the geometry of the exposure and the reflectivity and transmission measurement. From the grating transmission measurement (1.5-2 db decrease corresponding to 30-40% reflectivity in the 2.5-mm long grating), a modulated refractive index change of 0.12-0.14×10⁻³ is calculated at 1,550-nm. FIG. 7 shows the refractive index pattern grating formed in the bulk glass preform glass block. FIG. 7a is a cross-section showing the refractive index pattern grating in the bulk glass preform glass block.

[0076] While the UV exposure experiments described in this Example have used hydrogen loading to increase the photosensitivity of the glasses, it is noted that the glasses of this Example are also photosensitive in the absence of hydrogen and at low hydrogen loading levels. Glasses with no/low hydrogen loading may require a longer exposure time or higher exposure fluence to achieve a given index change.

[0077] Glass 4 b of the Composition Table is preferred composition of the invention. The weight percent batch composition was 35.8 wt. % SiO₂, 21.5 wt. % GeO₂, 4.48 wt. %, Al₂O₃, 3.38 wt. % F, 1.31 wt. Li₂O, and 33.5 wt. % B₂O₃. The batch material powders were ball milled to provide a homogeneous batch mix. For SiO₂, high purity silica sand powder, ach as IOTA-6 brand SiO₂ from the Unimin Corporation, Spruce Pine, N.C. 28777, was utilized with the high purity silica sand having a Fe impurity level of less than 0.1 ppm. For GeO₂, high purity germanium dioxide powder such as Chemical Grade No. 1-29/99.999% purity GeO₂ from the Electro-Optic Materials Dept., Eagle-Picher Technologies, LLC, Quapaw, Okla. 74363, was utilized with a purity having 0.1% maximum chloride content, ≦1 ppm Fe, ≦1 ppm Mg, ≦0.5 ppm Ni, and no detectable Pb (1 ppm detect limit), and no Zn (10 ppm detect limit). For aluminum, high purity aluminum oxide powder, such as Gamma brand aluminum oxide 99.999% from Alfa Aesar, A Johnson Mathey Company, Ward Hill, Mass. 01835, was utilized with the 99.999% purity. For aluminum, high purity aluminum fluoride was also used, such as Alufluor brand aluminum fluoride from LidoChem, Hazlet, N.J. 07730. For lithium, lithium carbonate was used, such as the Tech Grade 99+% purity Li₂CO₃ brand from FMC Corporation, Lithium Div., Gastonia, N.C. 28054, with a 99%+ purity, with Fe₂O₃ wt. ≦0.004 and a Cl wt. %≦0.01. Also for lithium, lithium nitrate crystal was used, such as available from VWR Scientific, Rochester, N.Y. 14603. For boron, boric oxide was used, such as Hi purity brand Anhydrous Boric Acid from Stetson Chemicals, Inc., 391 Exchange St., Buffalo, N.Y. 14204. The batch powder mixture after ball milling was loaded into a large vertically oriented platinum lines cylindrical furnace 100 as shown in FIG. 8. A total batch mass of 25 kg was used with furnace 100 in a semi-continuous run.

[0078] Batch powder mixture 101 was melted at 1,550° C. Furnace 100 includes a stirrer 102 for stirring glass melt 104 to provide a homogeneous glass melt. Furnace 100 includes a down corner 106 and a down corner orifice 108 for delivering a bulk glass body 110. Bulk glass bodies 110 were made with a general dimension of 105×4×4 inches (3.81×10.16×10.16 cm) and annealed at 414° C. The annealed bulk glass bodies 110 were cut, finished, and polished to provide small bulk glass bodies 120 having a rectangular block shape. Bulk glass bodies 120 had a dimension of 5×5×3 mm³. As shown in FIG. 9, bulk glass bodies 120 were loaded with molecular hydrogen (H₂) in a hydrogen pressure vessel 200 using hydrogen atmosphere 210 of about 100 atmospheres to provide H₂ loaded bulk glass body preforms 120.

[0079] Other exemplary glasses of the present invention have higher alumina and fluorine contents than the glasses of the Composition Table. For example, glass 18 has a composition including 34.7 wt % SiO₂, 11.2 wt % GeO₂, 16.4 wt % Al₂O₃, 1.66 wt % Na₂O, 12.9 wt % K₂O, 15.9 wt % B₂O₃, and 7.23 wt % F. Glass 19 has a composition including 34.51 wt % SiO₂, 13.6 wt % Al₂O₃, 1.32 wt % Na₂O, 10.8 wt % K₂O, 15.81 wt % B₂O₃, and 7.23 wt % F. The glasses were melted using methods analogous to those described above with reference to Glass Composition Table 1. These glasses have hydrogen-loaded and low/no hydrogen-loaded photosensitivities roughly equivalent to those described above.

[0080] The invention having been described in detail in connection through a discussion of exemplary embodiments, it is clear that modifications of the invention will be apparent to one having ordinary skill in the art having had the benefit of the present disclosure. Such modifications and variations are included in the scope of the appended claims. 

I claim:
 1. A meltable photosensitive glass having a molecular hydrogen content of ≧10¹⁷H₂ molecules/cm³.
 2. A glass as recited in claim 1, wherein the glass is a germanosilicate glass.
 3. A glass as recited in claim 1 wherein the glass comprises an alkali boro-alumino-silicate glass having a melting temperature ≦1,650° C., said alkali boro-alumino-silicate glass having a batch composition comprising ≦85 mole % SiO₂, ≧10 mole % B₂O₃, ≧2 mole % GeO₂, and a combined alkali and alumina content <20 mole % Al₂O₃+R₂O, said glass having a molecular hydrogen loadable level of at least 10¹⁸H₂ molecules/cm³.
 4. A glass as recited in claim 3, having a batch composition with >70 mole % SiO₂ and ≧25 mole % B₂O₃.
 5. A glass as recited in claim 1, wherein the glass is photosensitizable to light having a wavelength of less than 300 nm, and wherein said glass comprises 40-80 mole % SiO₂, 2-15 mole % GeO₂, 10-36 mole % B₂O₃, 1-6 mole % Al₂O₃, and 2-10 mole % R₂O wherein R is an alkali.
 6. A glass as recited in claim 5, wherein said glass comprising 42-73 mole % SiO₂, 2-15 mole % GeO₂, 20-36 mole % B₂O₃, 2-6 mole % Al₂O₃, and 2-8 mole % R₂O.
 7. A glass as recited in claim 5, wherein said glass comprising 42-67 mole % SiO₂, 2-15 mole % GeO₂, 25-36 mole % B₂O₃, 2-6 mole % Al₂O₃, and 2-6 mole % R₂O.
 8. A glass as recited in claim 5, wherein R is at least one alkali chosen from a group consisting of Na, Li, and K.
 9. A glass as recited in claim 5, having a transition metal contaminant level of ≦1 ppm by weight for transition metal contaminants.
 10. A glass as recited in claim 5, having a heavy metal contaminant level ≦1 ppm by weight for heavy metal.
 11. A glass as recited in claim 5, having a Fe content <1 ppm by weight Fe.
 12. A glass as recited in claim 5, having a Ti content <1 ppm by weight Ti.
 13. A glass as recited in claim 5, wherein said glass has a alkali/alumina ratio in the range of 1±0.5.
 14. A glass as recited in claim 5, having a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴.
 15. A glass as recited in claim 1, wherein said molecular hydrogen content is loaded in said glass and said content is ≧10¹⁸H₂ molecules/cm³.
 16. A glass as recited in claim 1, wherein said molecular hydrogen content is loaded in said glass and said content is ≧10¹⁹H₂ molecules/cm³.
 17. A glass as recited in claim 1, having a 300 nm absorption less than 20 dB/cm.
 18. A glass as recited in claim 1, said glass having a modulated refractive index Δn≧2×10⁻⁴.
 19. A glass as recited in claim 1, having a melting temperature ≦1,650° C.
 20. A glass as recited in claim 1, having a melting temperature ≦1,600° C.
 21. A glass as recited in claim 1, having a melting temperature ≦1,550° C.
 22. A glass as recited in claim 1, having a melting temperature ≦1,500° C.
 23. A glass as recited in claim 1, having a softening temperature <700° C.
 24. A glass as recited in claim 1, having a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴ when said molecular hydrogen content is >10¹⁹H₂ molecules/cm³.
 25. A glass as recited in claim 2, wherein said glass having an increased OH content when loaded with molecular hydrogen and exposed to UV radiation.
 26. A glass as recited in claim 2, wherein said glass having an OH range of about 100 to 1,000 OH ppm weight.
 27. A glass as recited in claim 1, wherein said glass comprises approximately 25 weight percent to approximately 45 weight % SiO₂, approximately 3 weight percent to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F.
 28. A glass as recited in claim 27, wherein said glass comprises approximately 30 weight % to approximately 40 weight % SiO₂.
 29. A glass as recited in claim 27 wherein said glass has a GeO₂ content of approximately 7 weight % to approximately 17 weight %.
 30. A glass as recited in claim 27 wherein said glass has a B₂O₃ content of approximately 10 weight % to approximately 22 weight %.
 31. A glass as recited in claim 27 wherein said glass has an Al₂O₃ content of approximately 10 weight % to approximately 19 weight %.
 32. A glass as recited in claim 27 wherein said glass has an R₂O content of approximately 10 weight % to approximately 20 weight %.
 33. A glass as recited in claim 27 wherein said glass has a F content of approximately 5 weight % to approximately 11 weight %.
 34. A glass as recited in claim 27, wherein said glass has an alkali/alumina ratio in the range of approximately 0.5 to approximately 1.5.
 35. A glass as recited in claim 1 having a fluorine content of ≦10 wt %.
 36. A glass as recited in claim 1 having a fluorine content of ≦6 wt %.
 37. A meltable photosensitive germanosilicate glass material having a hydrogen content less than approximately 10¹⁷H₂ molecules/cm³.
 38. A glass as recited in claim 37, wherein the glass comprises an alkali boro-alumino-silicate glass having a melting temperature ≦1,650° C., said alkali boro-alumino-silicate glass having a batch composition comprising ≦85 mole % SiO₂, ≧10 mole % B₂O₃, ≧2 mole % GeO₂, and a combined alkali and alumina content <20 mole % Al₂O₃+R₂O.
 39. A glass as recited in claim 38, having a batch composition with ≦70 mole % SiO₂ and ≧25 mole % B₂O₃.
 40. A glass as recited in claim 37, wherein the glass is photosensitizable to light having a wavelength of less than 300 nm, and wherein said glass comprises approximately 40 mole % to approximately 80 mole % SiO₂, approximately 2 mole % to approximately 15 mole % GeO₂, approximately 10 mole % to approximately 36 mole % B₂O₃, approximately 1 mole % to approximately 6 mole % Al₂O₃, and approximately 2 mole % to approximately 10 mole % R₂O wherein R is an alkali.
 41. A glass as recited in claim 40, wherein said glass comprises approximately 42 mole % to approximately 73 mole % SiO₂, approximately 2 mole % to approximately 15 mole % GeO₂, approximately 20 mole % to approximately 36 mole % B₂O₃, approximately 2 mole % to approximately 6 mole % Al₂O₃, and approximately 2 mole % to approximately 8 mole % R₂O.
 42. A glass as recited in claim 40, wherein said glass comprises approximately 42 mole % to approximately 67 mole % SiO₂, approximately 2 mole % to approximately 15 mole % GeO₂, approximately 25 mole % to approximately 36 mole % B₂O₃, approximately 2 mole % to approximately 6 mole % Al₂O₃, and approximately 2 mole % to approximately 6 mole % R₂O.
 43. A glass as recited in claim 40, wherein R is at least one alkali chosen from a group consisting essentially of Na, Li, and K.
 44. A glass as recited in claim 40, wherein said glass has an alkali/alumina ratio in the range of approximately 0.5 to approximately 1.5.
 45. A glass as recited in claim 40, having a below 300 nm wavelength induced modulated refractive index Δn>10⁻⁴.
 46. A glass as recited in claim 37 wherein the glass has a hydrogen content of less than approximately 10¹⁴ hydrogen molecules/Cm³.
 47. A glass as recited in claim 37, having a 300 nm absorption less than 20 dB/cm.
 48. A glass as recited in claim 37, said glass having a modulated refractive index Δn≧2×10⁻⁴.
 49. A glass as recited in claim 37, having a melting temperature ≦1,650° C.
 50. A glass as recited in claim 37, having a melting temperature ≦1,600° C.
 51. A glass as recited in claim 37, having a melting temperature ≦1,550° C.
 52. A glass as recited in claim 37, having a melting temperature ≦1,500° C.
 53. A glass as recited in claim 37, having a softening temperature <700° C.
 54. A glass as recited in claim 37, wherein said glass comprises approximately 25 weight % to approximately 45 weight % SiO₂, approximately 3 weight % to approximately 22 weight % GeO₂, approximately 7 weight % to approximately 28 weight % B₂O₃, approximately 6 weight % to approximately 22 weight % Al₂O₃, approximately 6 weight % to approximately 25 weight % R₂O wherein R is an alkali, and approximately 3 weight % to approximately 11 weight % F.
 55. A glass as recited in claim 54, wherein said glass comprises approximately 30 weight % to approximately 40 weight % SiO₂.
 56. A glass as recited in claim 54 wherein said glass has a GeO₂ content of approximately 7 weight % to approximately 17 weight %.
 57. A glass as recited in claim 54 wherein said glass has a B₂O₃ content of approximately 10 weight % to approximately 22 weight %.
 58. A glass as recited in claim 54 wherein said glass has an Al₂O₃ content of approximately 10 weight % to approximately 19 weight %.
 59. A glass as recited in claim 54 wherein said glass has an R₂O content of approximately 10 weight % to approximately 20 weight %.
 60. A glass as recited in claim 54 wherein said glass has a F content of approximately 5 weight % to approximately 11 weight %.
 61. A glass as recited in claim 54, wherein said glass has an alkali/alumina ratio in the range of approximately 0.5 to approximately 1.5.
 62. A method of making a refractive index pattern, the method comprising: providing a photosensitive glass having a 300 nm absorption less than 20 dB/cm; providing a below 300 nm radiation source and producing below 300 nm radiation; forming a pattern with said below 300 nm radiation; exposing said photosensitive bulk glass to said pattern to form a modulated refractive index pattern in said bulk glass.
 63. A method as recited in claim 62, wherein providing a photosensitive bulk glass includes providing an alkali boro-alumino-silicate glass.
 64. A method as recited in claim 62, wherein providing a photosensitive bulk glass includes providing a germanosilicate glass.
 65. A method as recited in claim 62, wherein providing a photosensitive bulk glass includes providing a glass body having a homogeneous composition.
 66. A method as recited in claim 62, wherein providing a photosensitive glass includes providing a non-sintered glass.
 67. A method as recited in claim 62, wherein providing a photosensitive glass includes providing a melted glass.
 68. A method as recited in claim 62, wherein providing a photosensitive glass includes providing an alkali boro-alumino-silicate glass batch, melting said glass batch to form an alkali boro-alumino-silicate glass melt.
 69. A method as recited in claim 62, wherein providing a photosensitive glass includes providing a molecular hydrogen loaded bulk glass.
 70. A method as recited in claim 62, wherein providing a photosensitive glass includes providing a melted glass and providing at least 10¹⁸H₂ molecules/cm³ into the glass.
 71. A method as recited in claim 62, wherein exposing to form a pattern in the glass includes a Δn≧10⁻⁴.
 72. A method of making a molecular hydrogen loadable photosensitive glass optical device preform, the method comprising: providing a germania silica glass having a transition metal contamination level≦1 ppm by weight for transition metals and a heavy metal contamination level≦1 ppm by weight for heavy metals; melting said silica glass batch to form a homogeneous glass melt; cooling said glass melt into UV transmitting bulk glass having a 300 nm absorption less than 20 dB/cm; forming said bulk glass into an optical device preform.
 73. A method as recited in claim 72, further including providing a molecular hydrogen content to a level of at least 10¹⁷H₂ molecules/cm³ in said glass.
 74. A method as recited in claim 72, wherein melting includes melting at a temperature ≦1,650° C.
 75. A method as recited in claim 72, wherein providing a silica glass batch includes providing an alkali boro-alumino-silicate glass batch.
 76. A method as recited in claim 72, wherein providing a silica glass batch includes providing a germanosilicate glass batch.
 77. A method as recited in claim 72, including pouring said glass melt.
 78. A method as recited in claim 72, including delivering said glass melt through an orifice.
 79. A method as recited in claim 72, wherein forming into an optical device preform includes forming a preform with a small dimension >5 μm.
 80. A photosensitive glass optical refractive index pattern preform for use with UV light in the formation of refractive index patterns, said preform comprised of an alkali boro-aluminio-silicate glass with a 300 nm absorption less than 20 dB/cm, said refractive index pattern preform having a UV wavelength inducable modulated refractive index Δn>10⁻⁵ with a molecular hydrogen level of at least 10¹⁸H₂ molecules/cm³.
 81. A refractive index pattern preform as recited in claim 80, having a UV wavelength inducable modulated refractive index Δn>10⁻⁴ with a molecular hydrogen level of at least 10¹⁹H₂ molecules/cm³.
 82. A refractive index pattern preform as recited in claim 80, wherein said alkali boro-alumino-silicate glass is a melted glass. 